Typical Properties
Melt Flow Rate (220 °C/10.0 kg)
4.9 g/10 min
Melt Flow Rate (230 °C/3.8 kg, Procedure A)
1.6 g/10 min
Density - Specific Gravity
1.08 g/cm³
Tensile Stress at Yield
41 MPa
Tensile Strength at Yield (50 mm/min)
43.0 MPa
Flexural Modulus (Injection Molded, Chord)
2340 MPa
Flexural Modulus (1.3 mm/min, Procedure B, Method I (3 point load), 1% Secant)
2130 MPa
Charpy Impact Strength - Notched (23 °C)
17 kJ/m²
Charpy Impact Strength - Notched (-30 °C)
9.5 kJ/m²
Notched Izod Impact Strength (23 °C)
19 kJ/m²
Notched Izod Impact Strength (-30 °C)
9.5 kJ/m²
Notched Izod Impact (-30 °C)
110 J/m
Notched Izod Impact (23 °C, Method A)
200 J/m
Rockwell Hardness (R-Scale)
111
Rockwell Hardness (R-Scale)
111
Vicat Softening Temperature
122 °C
Vicat Softening Temperature (Loading 1 (10 N))
125 °C
Deflection Temperature Under Load Unannealed (0.45 MPa)
111 °C
Deflection Temperature Under Load Unannealed (1.80 MPa)
94.6 °C
Deflection Temperature Under Load Unannealed (264 psi)
94.3 °C
Deflection Temperature Under Load Unannealed (66 psi)
110 °C
Coefficent of Linear Thermal Expansion (CLTE), Flow (TMA)
7.8E-05 cm/cm/°C
Coefficent of Linear Thermal Expansion (CLTE), Perpendicular (TMA)
9.1E-05 cm/cm/°C
Drying Temperature
82 to 90 °C
Drying Time
2.0 to 4.0 hr
Suggested Max Moisture
0.1 %
Rear Temperature
200 to 250 °C
Middle Temperature
200 to 250 °C
Front Temperature
200 to 250 °C
Mold Temperature
40 to 80 °C
Injection Rate
Moderate-Fast